Our 4 to 1 Epoxy Activator forms an easy to use 2 component 100 % solids epoxy system when mixed with either of our available epoxy resins in a ratio of four parts Resin ( A side ) to one part Activator (B side ) by volume. It Is significantly faster setting then our 3 to 1 system with the best chemical and solvent resistance and physical properties. When mixed with our Standard Epoxy Resin it forms a thicker high viscosity system more suited to adhesive bonding and casting applications and will form a hard strong plastic with excellent resistance to chemicals and solvents including hydrocarbon fuels and ethanol. When used with our Laminating Epoxy Resin it will form a thinner liquid more appropriate for wetting out fiberglass and other reinforcements it will have a slightly longer Gel Time and form a plastic with more flexibility, slightly less solvent resistance and lower HDT. Both systems cure to a tough, hard, blush free, amber colored plastic, with good physical properties excellent chemical and solvent resistance, good resistance to water and good adhesion to wood, glass, metals, and most other plastics.

As with all adhesive compounds bonding surfaces should be clean and free dirt or grease

 Our 5 to 1 Laminating system is a two component 100 % solids Epoxy resin system designed for coating, bonding, and the lamination of glass, carbon, or kevlar fibers as used in the production of composite plastic products. This material features an easy to use 5 to 1 by volume mix ratio that is (5 Parts Epoxy Resin to 1 Part of Activator by volume such as liquid ounces, pints, quarts, or liters). The material itself features easy wet out, rapid cure, and good adhesion to a variety of materials including wood, glass, metals and most other plastics. The material cures to a very rigid, hard, amber colored plastic, with a high Heat Distortion Temperature and will have good physical properties, good resistance to water, and excellent resistance to chemicals and solvents. Thin films cured in open air may blush .
As with all adhesive type compounds proper surface preparation is essential for good bond strength, recoating of the material should be accomplished before the material is fully cured after which sanding and solvent wash may be necessary for good secondary bonding.

  Our 5 to 1 Laminating system is a two component 100 % solids Epoxy resin system designed for coating, bonding, and the lamination of glass, carbon, or kevlar fibers as used in the production of composite plastic products. This material features an easy to use 5 to 1 by volume mix ratio that is (5 Parts Epoxy Resin to 1 Part of Activator by volume such as liquid ounces, pints, quarts, or liters). The material itself features easy wet out, rapid cure, and good adhesion to a variety of materials including wood, glass, metals and most other plastics. The material cures to a very rigid, hard, amber colored plastic, with a high Heat Distortion Temperature and will have good physical properties, good resistance to water, and excellent resistance to chemicals and solvents. Thin films cured in open air may blush . 
As with all adhesive type compounds proper surface preparation is essential for good bond strength, recoating of the material should be accomplished before the material is fully cured after which sanding and solvent wash may be necessary for good secondary bonding.

  Our 5 to 1 Laminating system is a two component 100 % solids Epoxy resin system designed for coating, bonding, and the lamination of glass, carbon, or kevlar fibers as used in the production of composite plastic products. This material features an easy to use 5 to 1 by volume mix ratio that is (5 Parts Epoxy Resin to 1 Part of Activator by volume such as liquid ounces, pints, quarts, or liters). The material itself features easy wet out, rapid cure, and good adhesion to a variety of materials including wood, glass, metals and most other plastics. The material cures to a very rigid, hard, amber colored plastic, with a high Heat Distortion Temperature and will have good physical properties, good resistance to water, and excellent resistance to chemicals and solvents. Thin films cured in open air may blush . 
As with all adhesive type compounds proper surface preparation is essential for good bond strength, recoating of the material should be accomplished before the material is fully cured after which sanding and solvent wash may be necessary for good secondary bonding.

  Our 5 to 1 Laminating system is a two component 100 % solids Epoxy resin system designed for coating, bonding, and the lamination of glass, carbon, or kevlar fibers as used in the production of composite plastic products. This material features an easy to use 5 to 1 by volume mix ratio that is (5 Parts Epoxy Resin to 1 Part of Activator by volume such as liquid ounces, pints, quarts, or liters). The material itself features easy wet out, rapid cure, and good adhesion to a variety of materials including wood, glass, metals and most other plastics. The material cures to a very rigid, hard, amber colored plastic, with a high Heat Distortion Temperature and will have good physical properties, good resistance to water, and excellent resistance to chemicals and solvents. Thin films cured in open air may blush . 
As with all adhesive type compounds proper surface preparation is essential for good bond strength, recoating of the material should be accomplished before the material is fully cured after which sanding and solvent wash may be necessary for good secondary bonding.

 FGCI Superbond Epoxy Adhesive is a two-component, 100% solid system designed for adhesive bonding and the fitting and fairing of a wide variety of substrates.

 The material features a highly thixotropic, paste-like consistency, which hangs well in thick sections on vertical and overhead surfaces.

 The material cures to a hard, blush-free, amber- colored, high-strength, moisture-resistant plastic with excellent adhesive properties.

 Additional recoating of this material should be done before the material is thoroughly cured.

 If the material has cured hard and tack-free, a light sanding and solvent wash is advisable before recoating.

 Epoxy cures faster at higher temperatures and in thicker layered applications.


Directions for Use:
Step 1: Required prep will vary according to application surface:
Ceramics, Composites, Plastics & Wood  Must be oil free and sanded 80 grit or rougher.
Glass  Must be sanded with 220 grit or lower until shine is removed.
Metals  All metals must be carefully degreased with trisodium phosphate (TSP). Depending on the type of metal, prep work may vary.
Step 2: Be sure to clean the application site, removing all dust and debris.
Step 3: FGCIs Superbond Base Resin may be used with any of the three Activators, which differ in curing time:
Standard Activator
Medium Activator
Fast Activator
Please refer to Properties Chart for gel time.
Step 4: Mix at a 1:1 ratio by volume or weight, equal parts Base and Activator.
Step 5: Stir thoroughly, being sure to scrape sides and bottom of container. For best results, do not mix more than a quart at a time.

 FGCI Superbond Epoxy Adhesive is a two-component, 100% solid system designed for adhesive bonding and the fitting and fairing of a wide variety of substrates.

 The material features a highly thixotropic, paste-like consistency, which hangs well in thick sections on vertical and overhead surfaces.

 The material cures to a hard, blush-free, amber- colored, high-strength, moisture-resistant plastic with excellent adhesive properties.

 Additional recoating of this material should be done before the material is thoroughly cured.

 If the material has cured hard and tack-free, a light sanding and solvent wash is advisable before recoating.

 Epoxy cures faster at higher temperatures and in thicker layered applications.


Directions for Use:
Step 1: Required prep will vary according to application surface:
Ceramics, Composites, Plastics & Wood  Must be oil free and sanded 80 grit or rougher.
Glass  Must be sanded with 220 grit or lower until shine is removed.
Metals  All metals must be carefully degreased with trisodium phosphate (TSP). Depending on the type of metal, prep work may vary.
Step 2: Be sure to clean the application site, removing all dust and debris.
Step 3: FGCIs Superbond Base Resin may be used with any of the three Activators, which differ in curing time:
Standard Activator
Medium Activator
Fast Activator
Please refer to Properties Chart for gel time.
Step 4: Mix at a 1:1 ratio by volume or weight, equal parts Base and Activator.
Step 5: Stir thoroughly, being sure to scrape sides and bottom of container. For best results, do not mix more than a quart at a time.

 FGCI Superbond Epoxy Adhesive is a two-component, 100% solid system designed for adhesive bonding and the fitting and fairing of a wide variety of substrates.

 The material features a highly thixotropic, paste-like consistency, which hangs well in thick sections on vertical and overhead surfaces.

 The material cures to a hard, blush-free, amber- colored, high-strength, moisture-resistant plastic with excellent adhesive properties.

 Additional recoating of this material should be done before the material is thoroughly cured.

 If the material has cured hard and tack-free, a light sanding and solvent wash is advisable before recoating.

 Epoxy cures faster at higher temperatures and in thicker layered applications.


Directions for Use:
Step 1: Required prep will vary according to application surface:
Ceramics, Composites, Plastics & Wood  Must be oil free and sanded 80 grit or rougher.
Glass  Must be sanded with 220 grit or lower until shine is removed.
Metals  All metals must be carefully degreased with trisodium phosphate (TSP). Depending on the type of metal, prep work may vary.
Step 2: Be sure to clean the application site, removing all dust and debris.
Step 3: FGCIs Superbond Base Resin may be used with any of the three Activators, which differ in curing time:
Standard Activator
Medium Activator
Fast Activator
Please refer to Properties Chart for gel time.
Step 4: Mix at a 1:1 ratio by volume or weight, equal parts Base and Activator.
Step 5: Stir thoroughly, being sure to scrape sides and bottom of container. For best results, do not mix more than a quart at a time.